The model printed with dual color pla filament has a dreamy and gorgeous bi-color appearance. Magic pla filament will appear in different colors at different angles.
Dreamy gorgeous two-tone appearance
Silk glossy texture
Easy to peel off
Not easy to break
eSUN Magic Silk PLA Filament 1.75mm 3D Printer Filament 1KG 2.2LBS Spool 3D Printing Material for 3D Print
Brand Name: ESUN
Model Number: ePLA-Silk Magic filament
About this item
【ePLA-Silk Magic filament】Gradually Dual Color make your print works more eye-catching and unique. Silk Magic PLA filament will definitely give you an outstanding silk glossy smooth appearance.
【Stable Dimensional Tolerance】Minimum tolerance and low warping to ensure consistent feeding and stable prints, no clogging, extremely high successful rate, resulting in printed parts that have an outstanding surface finish and are highly precise.
【Tangle Free & No Plugging】Full 1KG 3D printer filament reel, perfect roundness and very tight diameter tolerance, does not overlap or tangle. Melt well, no cracking, no bubbles. feed smoothly and constantly without clogging the nozzle or extruder.
【High Compatibility】Compatible with most of FDM 3D Printers, allow you to print multicolor in one small 3D printed item. Perfect for arts & crafts projects, vases and any other 3D printed items that could benefit from a unique silky smooth appearance.
【Vacuumed Sealed Packaging】Net Weight: 1KG. eSUN filament comes in a sealed vacuum bag with a desiccant bag to keep it dry and keep out dust and foreign particles, prevent nozzle jams and yield smooth 3D models.
|Filament Properties Table|
|3D PRINTING FILAMENT||eSilk-PLA Magic|
|Heat Distortion Temp(℃,0.45MPa)||54.7|
|Melt Flow Index(g/10min)||11.32（190℃/2.16kg）|
|Elongation at Break(%)||21.76|
|IZOD Impact Strength(kJ/㎡)||6.45|
|Recommended printing parameters|
|Extruder Temperature(℃)||190 – 230℃
|Bed temperature(℃)||45 – 60°C|
|Printing Speed||40 – 100mm/s|
|Recommended Build Surfaces||Masking paper, PVP solid glue, PEI|